Evaluación in vitro de la resistencia a la flexión de dos resinas compuestas nanohíbridas, OPALLIS de la FGM y NEOFIL de la Kerr
In the development of dentistry; techniques and materials are being renewed steadily; as well as the properties of the materials in dentistry, the flexural resistance or modulus of rupture is one of the properties present in the composite resins; for this reason, the present investigation was to det...
সংরক্ষণ করুন:
| প্রধান লেখক: | |
|---|---|
| বিন্যাস: | bachelorThesis |
| ভাষা: | spa |
| প্রকাশিত: |
2018
|
| বিষয়গুলি: | |
| অনলাইন ব্যবহার করুন: | http://dspace.unl.edu.ec/jspui/handle/123456789/21410 |
| ট্যাগগুলো: |
ট্যাগ যুক্ত করুন
কোনো ট্যাগ নেই, প্রথমজন হিসাবে ট্যাগ করুন!
|
ট্যাগ যুক্ত করুন | _version_ | 1857833045622521856 |
|---|---|
| author | Sarango Guaillas, José Luis |
| author_facet | Sarango Guaillas, José Luis |
| author_role | author |
| collection | Repositorio Universidad Nacional de Loja |
| dc.contributor.none.fl_str_mv | Valarezo Bravo, Tannya Lucila |
| dc.creator.none.fl_str_mv | Sarango Guaillas, José Luis |
| dc.date.none.fl_str_mv | 2018-10-13T00:53:53Z 2018-10-13T00:53:53Z 2018 |
| dc.format.none.fl_str_mv | 94 p. application/pdf |
| dc.identifier.none.fl_str_mv | http://dspace.unl.edu.ec/jspui/handle/123456789/21410 |
| dc.language.none.fl_str_mv | spa |
| dc.rights.none.fl_str_mv | http://creativecommons.org/licenses/by-nc-sa/3.0/ec/ info:eu-repo/semantics/openAccess |
| dc.source.none.fl_str_mv | reponame:Repositorio Universidad Nacional de Loja instname:Universidad Nacional de Loja instacron:UNL |
| dc.subject.none.fl_str_mv | RESINA COMPUESTA |
| dc.title.none.fl_str_mv | Evaluación in vitro de la resistencia a la flexión de dos resinas compuestas nanohíbridas, OPALLIS de la FGM y NEOFIL de la Kerr |
| dc.type.none.fl_str_mv | info:eu-repo/semantics/publishedVersion info:eu-repo/semantics/bachelorThesis |
| description | In the development of dentistry; techniques and materials are being renewed steadily; as well as the properties of the materials in dentistry, the flexural resistance or modulus of rupture is one of the properties present in the composite resins; for this reason, the present investigation was to determine the flexural strength of two composite resins, the nanohibridas opallis (FGM) and of the Neofil (KERR). The sample was composed of 30 blocks of composite resin nanohibridas, 15 blocks of the Opallis resin (FGM) and 15 blocks of Neofil resin (KERR) in both cases in tone A3; prepared under specifications of ISO 4049, 25mm in length, 2mm thick and 2mm wide. We considered two groups, group A: 15 Opallis resin blocks and group B: 15 blocks of Neofil resin. Subsequently, to blocks of resin underwent a test of flexion of 3 points in a universal testing machine Marshall model, at a speed of 1,7mm/min. The data collected from the study of flexion were analyzed using the statistical test T-Student, thereby obtaining values of 115,759Mpa for group A (opallis) and values of 92,972Mpa for group B (Kerr), which gives us a statistically significant difference of 19.685% of flexural resistance to l group A. The data collected from the study of flexion were analyzed using the statistical test T-Student, thereby obtaining values of 115,759Mpa for group A (opallis) and values of 92,972Mpa for group B (Kerr), which gives us a statistically significant difference of 19.685% of flexural resistance to l group A. Keywords: Bending, light cured, hybrid, nanoparticles, nanorelleno |
| eu_rights_str_mv | openAccess |
| format | bachelorThesis |
| id | UNL_7e1b3b3d4d7646d01b18b3dce3eb5c49 |
| instacron_str | UNL |
| institution | UNL |
| instname_str | Universidad Nacional de Loja |
| language | spa |
| network_acronym_str | UNL |
| network_name_str | Repositorio Universidad Nacional de Loja |
| oai_identifier_str | oai:dspace.unl.edu.ec:123456789/21410 |
| publishDate | 2018 |
| reponame_str | Repositorio Universidad Nacional de Loja |
| repository.mail.fl_str_mv | * |
| repository.name.fl_str_mv | Repositorio Universidad Nacional de Loja - Universidad Nacional de Loja |
| repository_id_str | 0 |
| rights_invalid_str_mv | http://creativecommons.org/licenses/by-nc-sa/3.0/ec/ |
| spelling | Evaluación in vitro de la resistencia a la flexión de dos resinas compuestas nanohíbridas, OPALLIS de la FGM y NEOFIL de la KerrSarango Guaillas, José LuisRESINA COMPUESTAIn the development of dentistry; techniques and materials are being renewed steadily; as well as the properties of the materials in dentistry, the flexural resistance or modulus of rupture is one of the properties present in the composite resins; for this reason, the present investigation was to determine the flexural strength of two composite resins, the nanohibridas opallis (FGM) and of the Neofil (KERR). The sample was composed of 30 blocks of composite resin nanohibridas, 15 blocks of the Opallis resin (FGM) and 15 blocks of Neofil resin (KERR) in both cases in tone A3; prepared under specifications of ISO 4049, 25mm in length, 2mm thick and 2mm wide. We considered two groups, group A: 15 Opallis resin blocks and group B: 15 blocks of Neofil resin. Subsequently, to blocks of resin underwent a test of flexion of 3 points in a universal testing machine Marshall model, at a speed of 1,7mm/min. The data collected from the study of flexion were analyzed using the statistical test T-Student, thereby obtaining values of 115,759Mpa for group A (opallis) and values of 92,972Mpa for group B (Kerr), which gives us a statistically significant difference of 19.685% of flexural resistance to l group A. The data collected from the study of flexion were analyzed using the statistical test T-Student, thereby obtaining values of 115,759Mpa for group A (opallis) and values of 92,972Mpa for group B (Kerr), which gives us a statistically significant difference of 19.685% of flexural resistance to l group A. Keywords: Bending, light cured, hybrid, nanoparticles, nanorellenoEn el desarrollo de la odontología; las técnicas y materiales se están renovando de manera constante; así como también las propiedades de los materiales en odontología, la resistencia flexural o módulo de ruptura es una de las propiedades presentes en las resinas compuestas; por ello en la presente investigación se propuso determinar la resistencia a la flexión de dos resinas compuestas nanohíbridas, Opallis de la (FGM) y Neofil de la (KERR). La muestra estuvo constituida por 30 bloques de resina compuestas nanohíbridas, 15 bloques de la resina Opallis (FGM) y 15 bloques de resina Neofil (KERR) en ambos casos en tono A3; elaborados bajo especificaciones de la norma ISO 4049, 25mm de longitud, 2mm de espesor y 2mm de ancho. Se consideraron dos grupos, grupo A: 15 bloques de resina Opallis y grupo B: 15 bloques de resina Neofil. Posteriormente, a los bloques de resina se les realizó un test de flexión de 3 puntos en una máquina de ensayos universales modelo Marshall, a una velocidad de 1,7mm/min. Los datos recopilados del estudio de flexión se analizaron mediante la prueba estadística T-Student, con lo cual se obteniendo valores de 115,759Mpa para el grupo A (Opallis) y valores de 92,972Mpa para el grupo B (Kerr), lo cual nos da una diferencia estadísticamente significante de 19,685% más de resistencia flexural para el grupo A. Basándose en estos resultados se pudo determinar que las resinas Opallis del grupo (A) presentan una mayor resistencia flexural que las resinas del grupo (B) Neofil, por lo tanto mayor módulo de elasticidad. Palabras claves: flexión, fotocurado, híbrido, nanopartículas, nanorelleno.Valarezo Bravo, Tannya Lucila2018-10-13T00:53:53Z2018-10-13T00:53:53Z2018info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/bachelorThesis94 p.application/pdfhttp://dspace.unl.edu.ec/jspui/handle/123456789/21410spahttp://creativecommons.org/licenses/by-nc-sa/3.0/ec/info:eu-repo/semantics/openAccessreponame:Repositorio Universidad Nacional de Lojainstname:Universidad Nacional de Lojainstacron:UNL2025-05-02T15:27:46Zoai:dspace.unl.edu.ec:123456789/21410Institucionalhttps://dspace.unl.edu.ec/Universidad públicahttps://unl.edu.ec/https://dspace.unl.edu.ec/oaiEcuador***opendoar:02025-05-02T15:27:46falseInstitucionalhttps://dspace.unl.edu.ec/Universidad públicahttps://unl.edu.ec/https://dspace.unl.edu.ec/oai*Ecuador***opendoar:02025-05-02T15:27:46Repositorio Universidad Nacional de Loja - Universidad Nacional de Lojafalse |
| spellingShingle | Evaluación in vitro de la resistencia a la flexión de dos resinas compuestas nanohíbridas, OPALLIS de la FGM y NEOFIL de la Kerr Sarango Guaillas, José Luis RESINA COMPUESTA |
| status_str | publishedVersion |
| title | Evaluación in vitro de la resistencia a la flexión de dos resinas compuestas nanohíbridas, OPALLIS de la FGM y NEOFIL de la Kerr |
| title_full | Evaluación in vitro de la resistencia a la flexión de dos resinas compuestas nanohíbridas, OPALLIS de la FGM y NEOFIL de la Kerr |
| title_fullStr | Evaluación in vitro de la resistencia a la flexión de dos resinas compuestas nanohíbridas, OPALLIS de la FGM y NEOFIL de la Kerr |
| title_full_unstemmed | Evaluación in vitro de la resistencia a la flexión de dos resinas compuestas nanohíbridas, OPALLIS de la FGM y NEOFIL de la Kerr |
| title_short | Evaluación in vitro de la resistencia a la flexión de dos resinas compuestas nanohíbridas, OPALLIS de la FGM y NEOFIL de la Kerr |
| title_sort | Evaluación in vitro de la resistencia a la flexión de dos resinas compuestas nanohíbridas, OPALLIS de la FGM y NEOFIL de la Kerr |
| topic | RESINA COMPUESTA |
| url | http://dspace.unl.edu.ec/jspui/handle/123456789/21410 |