“Implementación de un banco de partículas magnéticas fluorescentes para el laboratorio de la Universidad Técnica de Cotopaxi Extensión la Maná”.
The principal purpose of this project is the application of a fluorescent magnetic particle bank through the inspection of magnetic particles dissolved in water, in some times we find linear indications formed in the contour or foot of the weld. These indications may come from a real crack or a non-...
保存先:
| 第一著者: | |
|---|---|
| その他の著者: | |
| フォーマット: | bachelorThesis |
| 言語: | spa |
| 出版事項: |
2023
|
| 主題: | |
| オンライン･アクセス: | http://repositorio.utc.edu.ec/handle/27000/10179 |
| タグ: |
タグ追加
タグなし, このレコードへの初めてのタグを付けませんか!
|
タグ追加 | 要約: | The principal purpose of this project is the application of a fluorescent magnetic particle bank through the inspection of magnetic particles dissolved in water, in some times we find linear indications formed in the contour or foot of the weld. These indications may come from a real crack or a non-relevant indication caused by the weld geometry. The use of magnetism is mainly to evidence the presence of discontinuities that are open to the surface or very close to it through non-destructive testing with fluorescent magnetic particles to observe cracks or a non-relevant indication caused by the weld geometry. These tests determine the damage that exists in the test tube. The magnetization technique was performed in a dark room with ultraviolet illumination to achieve the current research specifications, applying ASTM E 1444 standards to establish the acceptance criteria for the different imperfections that may occur in the tests. It is essential to demagnetize and clean the parts after each test to avoid false results in the inspection. To visualize the magnetic field is attracted by magnetic field leakage caused by discontinuities. |
|---|