Análisis de material de aporte en el proceso de soldadura GTAW aplicado en el acero inoxidable martensítico AISI 420 y su influencia en las propiedades mecánicas

 

Authors
Ushiña Yagloa, José Rafael
Format
BachelorThesis
Status
publishedVersion
Description

El presente trabajo de investigación se basa en el proceso de soldadura GTAW realizada en juntas de acero inoxidable martensítico AISI 420 con material de aporte ER 308L y ER 312. Posteriormente se procedió a obtener probetas para realizar ensayos destructivos de impacto, dureza, doblez guiado y tracción; cuyos resultados han sido evaluados en este trabajo de investigación con la finalidad de determinar la influencia de los materiales de aporte en las propiedades mecánicas de las juntas soldadas. Este proyecto de investigación está fundamentado en el código AWS D1.6 “Structural Welding Code Stainless Steel” cuyo código establece disposiciones generales para realizar el proceso de soldadura en aceros inoxidables. Los ensayos se realizaron en la Escuela Superior Politécnica de Chimborazo en los laboratorios de la Escuela de Mecánica, para su desarrollo se contó con la guía y asesoramiento de los Técnicos de los diferentes laboratorios de materiales y ensayos; así como también se hizo uso de los equipos. Los datos obtenidos se tabularon y se procedió a la selección del mejor material de aporte mediante un análisis adecuado con la finalidad de determinar cuál presenta una mejor influencia en las propiedades del acero inoxidable martensítico AISI 420. Al finalizar el proyecto de investigación se obtuvo conclusiones y recomendaciones en base a los resultados obtenidos con la finalidad de contribuir a mejorar los procedimientos de soldadura en este tipo de material que pueden ser aplicados en el campo industrial.
The present research work is based on the GTAW welding process made in AISI 420 martensitic stainless steel joints with ER 308L and ER 312 filler material. Subsequently, samples were obtained to perform destructive impact tests, hardness, guided bending and traction; whose results have been evaluated in this research work with the purpose of determining the influence of the materials of contribution in the mechanical properties of the welded joints. This research project is based on the AWS code D1.6 "Structural Welding Code Stainless Steel" whose code establishes general provisions for carrying out the welding process in stainless steels. The tests were conducted at the Polytechnic School of Chimborazo in the laboratories of the school of mechanics, for its development was counted with the guidance and advice of the technicians of the different laboratories of materials and tests; as well as equipment was used. The data obtained were tabulated and the best contribution material was selected by means of a suitable analysis in order to determine which has a better influence on the properties of the AISI 420 martensitic stainless steel. At the end of the research project, conclusions and recommendations were obtained based on the results obtained in order to contribute to improve the welding procedures in this type of material that can be applied in the industrial field.

Publication Year
2018
Language
spa
Topic
ACERO INOXIDABLE
PROPIEDADES MECÁNICAS
MARTENSÍTICO
ACEROS ALEADOS
ACEROS INOXIDABLES
SOLDADURA GTAW
AISI 420
DUCTIBILIDAD